PRODUCT SEARCH
Print this page

308L CORE-BRIGHT

Core-Bright 308L was developed for flat and horizontal welding without the use of a shielding gas when joining 304 or 304L stainless steel.

Features

Welds types 301, 302, 304, 304L, 321, and 347 stainless steels and austenitic steels. Used extensively for welding chemical plant equipment.


* This item is subject to Industry Alloy Surcharges

308L CORE-BRIGHT
  • Industry
  • General Fabrication
  • Process
  • Petrochemical
  • Power Generation
  • Mobile Machinery
  • Rail Road Car
  • Welding Process
  • FCAW (Flux Core)

Classifications

  • Classifications/Approvals

    • AWS A5.22; E308LTO-3
    • CERTIFIED BY C.W.B.- AWS A5.22
    • ASME SFA 5.22

Properties

Typical Properties
Yield Strength 62 ksi, 427 MPa
Tensile Strength 90 ksi, 621 MPa
Elongation in 2" 40 %
Typical Undiluted Weld Metal Analysis  
C 0.025 %
Mn 1.5 %
Si 0.6 %
Cr 19.9 %
Ni 9.9 %
Ferrite 9 FN

SAW

Accessories

Depositions

Spray Transfer Deposition Table
Diameter ESO Wire Feed Speed Amps Volts Deposition Rate Average Deposition Efficiency
5/64 in, 2.0 mm 3/4 in., 19 mm 137 ipm, 348 cm/min 210 24 7.1 lbs./hr., 3.2 kg./hr. 86 %
181 ipm, 460 cm/min 250 26 9.5 lbs./hr., 4.3 kg./hr. 87 %
236 ipm, 599 cm/min 300 27 12.0 lbs./hr., 5.4 kg./hr. 85 %
3/32 in, 2.4 mm 1 in., 25 mm 112 ipm, 284 cm/min 250 26 8.4 lbs./hr., 3.8 kg./hr. 85 %
136 ipm, 345 cm/min 300 28 10.2 lbs./hr., 4.6 kg./hr. 85 %
184 ipm, 467 cm/min 350 29 13.9 lbs./hr., 6.3 kg./hr. 88 %
221 ipm, 561 cm/min 400 30 16.2 lbs./hr., 7.3 kg./hr. 85 %
273 ipm, 693 cm/min 450 30 20.6 lbs./hr., 9.3 kg./hr. 85 %
1-1/2 in., 38 mm 133 ipm, 338 cm/min 250 26 10.0 lbs./hr., 4.5 kg./hr. 89 %
178 ipm, 402 cm/min 300 28 13.5 lbs./hr., 6.1 kg./hr. 89 %
227 ipm, 577 cm/min 350 29 17.1 lbs./hr., 7.8 kg./hr. 87 %
302 ipm, 767 cm/min 400 30 22.7 lbs./hr., 10.3 kg./hr. 87 %
343 ipm, 871 cm/min 450 30 25.9 lbs./hr., 11.7 kg./hr. 87 %

Extra Info