DUAL SHIELD II 70 Ultra

Dual Shield II 70 Ultra is an all-position flux cored wire that displays exceptional impact properties in both as-welded and stress-relieved conditions.

Find nearest dealer
Product Data Sheet

Features

Dual Shield II 70 Ultra is an all-position flux cored wire that displays exceptional impact properties when used with 75% Ar/25% CO2. The improved properties qualify this wire to the Navy's "HY" classification. The "Ultra" series produces smoother arc characteristics and lower welding fumes. Dual Shield II 70 Ultra was developed to join low and medium carbon steel. The Military classification allows Dual Shield II 70 Ultra to be used for attaching steels of less than 81 ksi (560 MPa) yield to HY-80 and HY-100. Commercial applications include construction, shipbuilding, railcar, and heavy equipment industries.

Dual Shield II 70 Ultra
  • Industry
  • Rail Road Car
  • Bridge Construction
  • Mobile Machinery
  • Civil Construction
  • Shipbuilding
  • General Fabrication
  • Welding Process
  • FCAW (Flux Core)

Classifications

  • Classifications/Approvals

    • AWS A5.20; E71T-1M/T-12M
    • L.R.- 3S,3YS(H10)
    • QPL-24403/1; MIL-71T-1-HYM
    • QPL-24403/1; MIL-71T-1M
    • A.B.S.- 3SA,3YSA(H5)
    • CERTIFIED BY C.W.B.- CSA W48
    • G.L.- 3YH10S
    • B.V.- SA3YM(HH)
    • D.N.V.- III YMS(H10)
    • ASME SFA 5.20
    • DEUTSCHE BAHN
    • CONTROLAS
    • TUV

Properties

Typical Properties
As Welded 75% Ar / 25% CO2  
Yield Strength 72 ksi, 490 MPa
Tensile Strength 81 ksi, 560 MPa
Reduction in Area 75 %
Elongation in 2" 29 %
Typical Charpy V-Notch Impact Properties  
Testing Temperature 0ºF (-18ºC)  
As Welded 75% Ar / 25% CO2 117 ft.-lbs., 159 J
Testing Temperature -20ºF (-29ºC)  
As Welded 75% Ar / 25% CO2 70 ft.-lbs., 95 J
Typical Undiluted Weld Metal Analysis  
75% Ar / 25% CO2  
C 0.04 %
Mn 1.0 %
Si 0.4 %
P 0.008 %
S 0.009 %

SAW

Accessories

Depositions

Deposition Table
Diameter Amps Volts Wire Feed Speed Deposition Rate Efficiency
.045 in, 1.2 mm 145 A 22 V 200 ipm, 508 cm/min 3.94 lbs./hr., 1.79 kg./hr. 86.15 %
210 A 23 V 300 ipm, 762 cm/min 5.99 lbs./hr., 2.72 kg./hr. 85.51 %
247 A 24.5 V 400 ipm, 1016 cm/min 8.10 lbs./hr., 3.68 kg./hr. 87.55 %
275 A 26 V 500 ipm, 1270 cm/min 9.52 lbs./hr., 4.33 kg./hr. 82.08 %
325 A 27.5 V 600 ipm, 1524 cm/min 12.38 lbs./hr., 5.63 kg./hr. 88.39 %
.052 in, 1.4 mm 150 A 21 V 150 ipm, 381 cm/min 4.01 lbs./hr., 1.82 kg./hr. 83.25 %
192 A 22 V 200 ipm, 508 cm/min 5.44 lbs./hr., 2.48 kg./hr. 84.71 %
262 A 23.5 V 300 ipm, 762 cm/min 8.12 lbs./hr., 3.69 kg./hr. 85.48 %
308 A 25 V 400 ipm, 1016 cm/min 10.92 lbs./hr., 4.97 kg./hr. 86.31 %
356 A 26.5 V 500 ipm, 1270 cm/min 14.00 lbs./hr., 6.37 kg./hr. 88.12 %
396 A 28 V 600 ipm, 1524 cm/min 16.81 lbs./hr., 7.65 kg./hr. 87.77 %
1/16 in, 1.6 mm 203 A 23 V 150 ipm, 381 cm/min 5.63 lbs./hr., 2.56 kg./hr. 87.15 %
298 A 24.5 V 250 ipm, 635 cm/min 9.33 lbs./hr., 4.25 kg./hr. 87.56 %
340 A 25.5 V 300 ipm, 762 cm/min 11.10 lbs./hr., 5.05 kg./hr. 87.68 %
375 A 26 V 350 ipm, 889 cm/min 13.24 lbs./hr., 6.02 kg./hr. 88.35 %
408 A 27.5 V 400 ipm, 1016 cm/min 14.49 lbs./hr., 6.59 kg./hr. 85.66 %
469 A 29 V 500 ipm, 1270 cm/min 18.93 lbs./hr., 8.62 kg./hr. 89.10 %

Extra Info

Shielding Gas

75% Argon / 25% CO2