ATOM ARC 8018-B6L
Atom Arc 8018-B6L deposits a low carbon 5% Cr - 0.5% Mo weld metal. This electrode is excellent for the petrochemical and petroleum industries where resistance to hydrogen attack is required.
Features
Atom Arc 8018-B6L deposits a low carbon 5% Cr, 0.5% Mo weld metal. It is designed for welding ASTM A200-T5, A335-P5, A387-Gr5 and similar steels. Applications tend to be in the petrochemical and petroleum industries, especially where hydrogen attack accelerates metal failure. Additionally, these steels are used in pressure vessels and piping for high temperature service.
View large imageClassifications
Classifications/Approvals
- MILITARY MIL-22200/8; MIL-E-502-15
- SFA/AWS A5.5; E8018-B6LH4R
Properties
| Stress Relieved 1 hr. @ 1375ºF (746ºC) | |
|---|---|
| Yield Strength | 95 ksi, 655 MPa |
| Tensile Strength | 81 ksi, 558 MPa |
| Elongation | 25 % |
| Typical Undiluted Weld Metal Analysis | |
| C | 0.04 % |
| Mn | 0.6 % |
| Si | 0.6 % |
| P | 0.015 % |
| S | 0.011 % |
| Cr | 5.4 % |
| Mo | 0.6 % |
Part No.
| Part No. | Model / Product Description | UPC |
|---|---|---|
| 255187809 | AA 8018-B6L 3/32X14X10#HS | 662303041342 |
| 255187817 | AA 8018-B6L 1/8X14X10#HS | 662303041359 |
| 255187825 | AA 8018-B6L 5/32X14X10#HS | 662303041366 |
| 255187833 | AA 8018-B6L 3/16X14X10#HS | 662303041373 |
| 255187841 | AA 8018-B6L 1/4X18X10#HS | 662303041380 |
| 255187759 | AA 8018-B6L 1/4X18X10#HS XF | 662303081171 |
| 255187767 | AA 8018-B6L 1/8X14X10#HS XF | 662303081140 |
| 255187775 | AA 8018-B6L 3/16X14X10#HS XF | 662303081164 |
| 255187783 | AA 8018-B6L 3/32X14X10#HS XF | 662303081133 |
| 255187791 | AA 8018-B6L 5/32X14X10#HS XF | 662303081157 |
SAW
Accessories
Depositions/Paramaters
| Diameter | Optimal Amperage | Range Amperage | Deposition Rate | Efficiency |
|---|---|---|---|---|
| 3/32 in, 2.4 mm | 90 A | 70 - 100 | 1.7 lbs./hr., 0.8 kg./hr. | 66.3 % |
| 1/8 in, 3.2 mm | 120 A | 90 - 160 | 2.6 lbs./hr., 1.2 kg./hr. | 71.6 % |
| 140 A | 90 - 160 | 2.7 lbs./hr., 1.2 kg./hr. | 70.9 % | |
| 5/32 in, 4.0 mm | 140 A | 130 - 220 | 3.1 lbs./hr., 1.4 kg./hr. | 75 % |
| 170 A | 130 - 220 | 3.8 lbs./hr., 1.7 kg./hr. | 73.5 % | |
| 3/16 in, 4.8 mm | 200 A | 200 - 300 | 4.9 lbs./hr., 2.2 kg./hr. | 76.4 % |
| 250 A | 200 - 300 | 5.4 lbs./hr., 2.4 kg./hr. | 74.6 % | |
| 7/32 in, 5.6 mm | 250 A | 250 - 350 | 6.5 lbs./hr., 2.9 kg./hr. | 75 % |
| 300 A | 250 - 350 | 7.2 lbs./hr., 3.3 kg./hr. | 74 % | |
| 1/4 in, 6.4 mm | 300 A | 300 - 400 | 7.7 lbs./hr., 3.5 kg./hr. | 78 % |
| 350 A | 300 - 400 | 8.7 lbs./hr., 3.9 kg./hr. | 77 % |
Extra Info
The recommended preheat temperature for 5CrMo steels is 400-500°F depending on thickness. Post weld heat treatment is generally required.