Atom Arc 8018-C1 is an all-position low hydrogen electrode that deposits weld metal containing nominal 2.3% Ni in applications that require low temperature toughness.
Features
Atom Arc 8018-C1 electrodes deposit weld metal which contains nominal 2.33% Ni. Their principal use is in the welding of nickel-bearing steels for low temperature applications where toughness of the weld metal at low temperatures is important.
View large imageClassifications
Classifications/Approvals
- ASME SFA 5.5
- A.B.S.- 3Y
- L.R.- 3m,3Ym(H15)
Properties
| As Welded | |
|---|---|
| Yield Strength | 80 ksi, 550 MPa |
| Tensile Strength | 90 ksi, 620 MPa |
| Elongation in 2" | 30 % |
| Stress Relieved 1 hr. @ 1150ºF (621ºC) | |
| Yield Strength | 75 ksi, 515 MPa |
| Tensile Strength | 86 ksi, 595 MPa |
| Reduction in Area | 74 % |
| Elongation in 2" | 30 % |
| Typical Charpy V-Notch Impact Properties | |
| Testing Temperature -75ºF (-59ºC) | |
| As Welded | 47 ft.-lbs., 64 J |
| Stress Relieved 1 hr. @ 1150ºF (621ºC) | 64 ft.-lbs., 87 J |
| Typical Undiluted Weld Metal Analysis | |
| C | .04 % |
| Mn | 1.1 % |
| Si | .3 % |
| P | 0.011 % |
| S | 0.009 % |
| Ni | 2.4 % |
Part No.
| Part No. | Model / Product Description | UPC |
|---|---|---|
| 255161416 | AA 8018-C1 1/4X18X50#HS | 662303018146 |
| 255161812 | AA 8018-C1 1/8X14X50#HS | 662303018153 |
| 255163115 | AA 8018-C1 3/16X14X50#HS | 662303018221 |
| 255163214 | AA 8018-C1 3/32X14X50#HS | 662303018252 |
| 255165318 | AA 8018-C1 5/32X14X50#HS | 662303018269 |
| 255167314 | AA 8018-C1 7/32X18X50#HS | 662303018283 |
| 255161820 | AA 8018-C1 1/8X14X10#HS | 662303018160 |
| 255163123 | AA 8018-C1 3/16X14X10#HS | 662303018238 |
| 255163206 | AA 8018-C1 3/32X14X10#HS | 662303018245 |
| 255165326 | AA 8018-C1 5/32X14X10#HS | 662303018276 |
SAW
Accessories
Depositions/Paramaters
| Diameter | Optimal Amperage | Range Amperage | Deposition Rate | Efficiency |
|---|---|---|---|---|
| 3/32 in, 2.4 mm | 90 A | 70 - 100 | 1.7 lbs./hr., 0.8 kg./hr. | 66.3 % |
| 1/8 in, 3.2 mm | 120 A | 90 - 160 | 2.6 lbs./hr., 1.2 kg./hr. | 71.6 % |
| 140 A | 90 - 160 | 2.7 lbs./hr., 1.2 kg./hr. | 70.9 % | |
| 5/32 in, 4.0 mm | 140 A | 130 - 220 | 3.1 lbs./hr., 1.4 kg./hr. | 75 % |
| 170 A | 130 - 220 | 3.8 lbs./hr., 1.7 kg./hr. | 73.5 % | |
| 3/16 in, 4.8 mm | 200 A | 200 - 300 | 4.9 lbs./hr., 2.2 kg./hr. | 76.4 % |
| 250 A | 200 - 300 | 5.4 lbs./hr., 2.4 kg./hr. | 74.6 % | |
| 7/32 in, 5.6 mm | 250 A | 250 - 350 | 6.5 lbs./hr., 2.9 kg./hr. | 75 % |
| 300 A | 250 - 350 | 7.2 lbs./hr., 3.3 kg./hr. | 74 % | |
| 1/4 in, 6.4 mm | 300 A | 300 - 400 | 7.7 lbs./hr., 3.5 kg./hr. | 78 % |
| 350 A | 300 - 400 | 8.7 lbs./hr., 3.9 kg./hr. | 77 % |
Extra Info
Preheat should be used on hardenable steels to prevent the formation of a hard heat-affected zone. Preheat may also be required in welding heavy sections.