ATOM ARC 10018
Atom Arc 10018 is an all-position low hydrogen electrode used primarily for applications requiring weld joints of at least 100 ksi (690 MPa) tensile strength, good ductility and crack resistance.
Features
Atom Arc 10018 electrodes are used primarily for applications which require weld joints of at least 100 ksi (690 MPa) tensile strength, good ductility and crack resistance. Good notch toughness at temperatures as low as -60ºF (-51ºC) is possible with this electrode. Atom Arc 10018 can be used to weld HY-80 and T-1 steel.
View large imageClassifications
Classifications/Approvals
- AWS A5.5; E10018-MH4R
- ASME SFA 5.5
Properties
| As Welded | |
|---|---|
| Yield Strength | 99 ksi, 685 MPa |
| Tensile Strength | 108 ksi, 745 MPa |
| Reduction in Area | 64 % |
| Elongation in 2" | 24 % |
| Typical Charpy V-Notch Impact Properties | |
| Testing Temperature -40ºF (-40ºC) | |
| As Welded | 46 ft.-lbs., 62 J |
| Testing Temperature -60ºF (-51ºC) | |
| As Welded | 28 ft.-lbs., 38 J |
| Typical Undiluted Weld Metal Analysis | |
| C | .051 % |
| Mn | 1.46 % |
| Si | .31 % |
| P | .013 % |
| S | .011 % |
| Ni | 1.72 % |
| Mo | .27 % |
Part No.
| Part No. | Model / Product Description | UPC |
|---|---|---|
| 255081416 | AA 10018 1/4X18X50#HS | 662303017538 |
| 255081713 | AA 10018 3/32X14X50#HS | 662303017552 |
| 255081812 | AA 10018 1/8X14X50#HS | 662303017569 |
| 255083115 | AA 10018 3/16X14X50#HS | 662303017583 |
| 255085318 | AA 10018 5/32X14X50#HS | 662303017606 |
| 255087314 | AA 10018 7/32X18X50#HS | 662303017620 |
| 255081820 | AA 10018 1/8X14X10#HS | 662303017576 |
| 255083123 | AA 10018 3/16X14X10#HS | 662303017590 |
| 255085326 | AA 10018 5/32X14X10#HS | 662303017613 |
SAW
Accessories
Depositions/Paramaters
| Diameter | Optimal Amperage | Range Amperage | Deposition Rate | Efficiency |
|---|---|---|---|---|
| 3/32 in, 2.4 mm | 90 A | 70 - 100 | 1.7 lbs./hr., 0.8 kg./hr. | 66.3 % |
| 1/8 in, 3.2 mm | 120 A | 90 - 160 | 2.6 lbs./hr., 1.2 kg./hr. | 71.6 % |
| 140 A | 90 - 160 | 2.7 lbs./hr., 1.2 kg./hr. | 70.9 % | |
| 5/32 in, 4.0 mm | 140 A | 130 - 220 | 3.1 lbs./hr., 1.4 kg./hr. | 75 % |
| 170 A | 130 - 220 | 3.8 lbs./hr., 1.7 kg./hr. | 73.5 % | |
| 3/16 in, 4.8 mm | 200 A | 200 - 300 | 4.9 lbs./hr., 2.2 kg./hr. | 76.4 % |
| 250 A | 200 - 300 | 5.4 lbs./hr., 2.4 kg./hr. | 74.6 % | |
| 7/32 in, 5.6 mm | 250 A | 250 - 350 | 6.5 lbs./hr., 2.9 kg./hr. | 75 % |
| 300 A | 250 - 350 | 7.2 lbs./hr., 3.3 kg./hr. | 74 % | |
| 1/4 in, 6.4 mm | 300 A | 300 - 400 | 7.7 lbs./hr., 3.5 kg./hr. | 78 % |
| 350 A | 300 - 400 | 8.7 lbs./hr., 3.9 kg./hr. | 77 % |
Extra Info
Preheat should be used on hardenable steels to prevent the formation of a hard heat-affected zone. Preheat may also be required in welding heavy section
Complementary Products
Seismic Data
All listed prices are in U.S. dollars and represent the Manufacturer's Suggested Retail Price (MSRP) for sale in the United States. Actual selling price will be determined by the Distributor. Prices are subject to change without notice.