ATOM ARC 10018-MM
Atom Arc 10018-MM is an all-position low hydrogen electrode used to weld low-alloy, high tensile steels where welds of 100 ksi (690 MPa) minimum tensile strength are required.
Features
Atom Arc 10018-MM electrodes are used to weld low-alloy, high-tensile steels where welds of 100 ksi (690 MPa) minimum tensile strength is required. This electrode is recommended for use in the weld repair and fabrication of Mn-Mo steel castings and armor plate.
View large imageClassifications
Classifications/Approvals
- ASME SFA 5.5
Properties
| Stress Relieved 1 hr. @ 1150ºF (621ºC) | |
|---|---|
| Yield Strength | 93 ksi, 640 MPa |
| Tensile Strength | 104 ksi, 715 MPa |
| Reduction in Area | 68 |
| Elongation in 2" | 24 % |
| Typical Charpy V-Notch Impact Properties | |
| Testing Temperature -60ºF (-51ºC) | |
| Stress Relieved 1 hr. @ 1150ºF (621ºC) | 24 ft.-lbs., 35 J |
| Typical Undiluted Weld Metal Analysis | |
| C | .082 % |
| Mn | 1.82 % |
| Si | 0.33 % |
| P | .015 % |
| S | .011 % |
| Mo | .37 % |
Part No.
| Part No. | Model / Product Description | UPC |
|---|---|---|
| 255091415 | AA 10018-MM 1/4X18X50#HS | 662303017712 |
| 255091811 | AA 10018-MM 1/8X14X50#HS | 662303017736 |
| 255093114 | AA 10018-MM 3/16X14X50#HS | 662303017750 |
| 255095317 | AA 10018-MM 5/32X14X50#HS | 662303017774 |
| 255097313 | AA 10018-MM 7/32X18X50#HS | 662303017798 |
| 255097339 | AA 10018-MM 3/32X14X50#HS | 662303017804 |
| 255091829 | AA 10018-MM 1/8X14X10#HS | 662303017743 |
| 255093122 | AA 10018-MM 3/16X14X10#HS/60CT | 662303017767 |
| 255095325 | AA 10018-MM 5/32X14X10#HS/60CT | 662303017781 |
SAW
Accessories
Depositions/Paramaters
| Diameter | Optimal Amperage | Range Amperage | Deposition Rate | Efficiency |
|---|---|---|---|---|
| 3/32 in, 2.4 mm | 90 A | 70 - 100 | 1.7 lbs./hr., 0.8 kg./hr. | 66.3 % |
| 1/8 in, 3.2 mm | 120 A | 90 - 160 | 2.6 lbs./hr., 1.2 kg./hr. | 71.6 % |
| 140 A | 90 - 160 | 2.7 lbs./hr., 1.2 kg./hr. | 70.9 % | |
| 5/32 in, 4.0 mm | 140 A | 130 - 220 | 3.1 lbs./hr., 1.4 kg./hr. | 75 % |
| 170 A | 130 - 220 | 3.8 lbs./hr., 1.7 kg./hr. | 73.5 % | |
| 3/16 in, 4.8 mm | 200 A | 200 - 300 | 4.9 lbs./hr., 2.2 kg./hr. | 76.4 % |
| 250 A | 200 - 300 | 5.4 lbs./hr., 2.4 kg./hr. | 74.6 % | |
| 7/32 in, 5.6 mm | 250 A | 250 - 350 | 6.5 lbs./hr., 2.9 kg./hr. | 75 % |
| 300 A | 250 - 350 | 7.2 lbs./hr., 3.3 kg./hr. | 74 % | |
| 1/4 in, 6.4 mm | 300 A | 300 - 400 | 7.7 lbs./hr., 3.5 kg./hr. | 78 % |
| 350 A | 300 - 400 | 8.7 lbs./hr., 3.9 kg./hr. | 77 % |
Extra Info
Preheat should be used on hardenable steels to prevent the formation of a hard heat-affected zone. Preheat may also be required in welding heavy sections