DUAL SHIELD II 110
Dual Shield II 110 is an all-position flux cored wire which produces a smooth spray-like transfer, low spatter levels, easy slag removal and good arc direction.
Features
Dual Shield II 110 is an all-position flux cored electrode which produces a smooth spray-like transfer, low spatter levels, low diffusible hydrogen levels, easy slag removal and good arc direction. Dual Shield II 110 was designed to join high strength steel such as HY-100 and T-1 in the as welded or stress relieved condition using 75% Ar / 25% CO2 shielding gas. It is well suited for joining high tensile steels that will be used in low temperatures. The weld metal analysis is similar to an E11018-M low hydrogen electrode.
View large imageClassifications
Classifications/Approvals
- A.B.S.- AWS A5.29; E111T1-K3M
- AWS A5.29; E111T1-K3CH4/K3MH4
- ASME SFA 5.29
Properties
| As Welded 75% Ar / 25% CO2 | |
|---|---|
| Yield Strength | 110 ksi, 760 MPa |
| Tensile Strength | 120 ksi, 830 MPa |
| Reduction in Area | 54 % |
| Elongation in 2" | 19 % |
| Stress Relieved 8 hrs. @ 1150ºF (621ºC) 75% Ar / 25% CO2 | |
| Yield Strength | 108 ksi, 745 MPa |
| Tensile Strength | 116 ksi, 800 MPa |
| Reduction in Area | 56 % |
| Elongation in 2" | 19 % |
| Typical Charpy V-Notch Impact Properties | |
| Testing Temperature 0ºF (-18ºC) | |
| As Welded 75% Ar / 25% CO2 | 40 ft.-lbs., 54 J |
| Stress Relieved 8 hrs. @ 1150ºF (621ºC) 75% Ar / 25% CO2 | 29 ft.-lbs., 39 J |
| Testing Temperature -20ºF (-29ºC) | |
| As Welded 75% Ar / 25% CO2 | 36 ft.-lbs., 49 J |
| Stress Relieved 8 hrs. @ 1150ºF (621ºC) 75% Ar / 25% CO2 | 27 ft.-lbs., 37 J |
| Testing Temperature -60ºF (-51ºC) | |
| As Welded 75% Ar / 25% CO2 | 26 ft.-lbs., 35 J |
| Stress Relieved 8 hrs. @ 1150ºF (621ºC) 75% Ar / 25% CO2 | 21 ft.-lbs., 28 J |
| Typical Undiluted Weld Metal Analysis | |
| 75% Ar / 25% CO2 | |
| C | .05 % |
| Mn | 1.91 % |
| Si | .43 % |
| P | .013 % |
| S | .010 % |
| Ni | 1.74 % |
| Mo | 0.39 % |
Part No.
SAW
Accessories
Depositions/Paramaters
| Diameter | Amps | Volts | Wire Feed Speed | Deposition Rate | Efficiency |
|---|---|---|---|---|---|
| .045 in, 1.2 mm | 150 A A | 28 | 200 ipm, 508 cm/min | 4.2 lbs./hr., 1.91 kg./hr. | 86 % |
| 210 A A | 29 | 300 ipm, 762 cm/min | 6.3 lbs./hr., 2.86 kg./hr. | 86 % | |
| 250 A A | 30 | 400 ipm, 1016 cm/min | 8.5 lbs./hr., 3.86 kg./hr. | 87 % | |
| 290 A A | 33 | 500 ipm, 1270 cm/min | 10.7 lbs./hr., 4.85 kg./hr. | 87 % | |
| 330 A A | 34 | 600 ipm, 1524 cm/min | 12.7 lbs./hr., 5.76 kg./hr. | 87 % | |
| .052 in, 1.4 mm | 155 A A | 25 | 150 ipm, 381 cm/min | 4.4 lbs./hr., 2 kg./hr. | 87 % |
| 245 A A | 28 | 250 ipm, 635 cm/min | 7.3 lbs./hr., 3.31 kg./hr. | 86 % | |
| 310 A A | 33 | 350 ipm, 889 cm/min | 10.2 lbs./hr., 4.63 kg./hr. | 85 % | |
| 360 A A | 36 | 450 ipm, 1143 cm/min | 13.3 lbs./hr., 6.03 kg./hr. | 85 % | |
| 430 A A | 37 | 600 ipm, 1524 cm/min | 17.6 lbs./hr., 7.98 kg./hr. | 87 % | |
| 1/16 in, 1.6 mm | 190 A A | 27 | 150 ipm, 38 cm/min | 6.1 lbs./hr., 2.77 kg./hr. | 87 % |
| 300 A A | 30 | 250 ipm, 635 cm/min | 10.2 lbs./hr., 4.63 kg./hr. | 87 % | |
| 365 A A | 33 | 300 ipm, 762 cm/min | 12.3 lbs./hr., 5.58 kg./hr. | 86 % | |
| 410 A A | 33 | 350 ipm, 889 cm/min | 14 lbs./hr., 6.35 kg./hr. | 88 % | |
| 450 A A | 33 | 400 ipm, 1016 cm/min | 16.1 lbs./hr., 7.3 kg./hr. | 87 % | |
| 500 A A | 39 | 500 ipm, 1270 cm/min | 20.1 lbs./hr., 9.11 kg./hr. | 87 % |
Extra Info
Shielding Gas
75% Argon/25% CO2
100% CO2