SPOOLARC 95
Spoolarc 95 is Military grade high strength wire used to weld HY-80 steels.
Features
Spoolarc 95 is Military grade high strength wire used to weld HY-80 steels.
Applications for Spoolarc 95 include military tanks, ships and submarines.
View large imageClassifications
Classifications/Approvals
- AWS A5.23; EM2
- MIL-E-23765/2; MIL-E-100S-1
Properties
| Yield Strength | 95,000 ksi, 126 MPa |
|---|---|
| Tensile Strength | 105,000 ksi, 725 MPa |
| Elongation in 2" | 23 % |
| Typical Charpy V-Notch Impact Properties | |
| Testing Temperature 0°F (-18°C) | 93 ft.-lbs., 126 J |
| Testing Temperature -60ºF (-51ºC) | 65 ft.-lbs., 88 J |
| Typical Undiluted Weld Metal Analysis | |
| C | 0.07 % |
| Mn | 1.40 % |
| Si | 0.35 % |
| P | 0.008 % |
| S | 0.007 % |
| Cr | 0.20 % |
| Ni | 1.80 % |
| Mo | 0.35 % |
Part No.
| Part No. | Model / Product Description | UPC |
|---|---|---|
| 2296F10 | 95 CU 3/32X800#DR | 662303668563 |
| 2296F14 | 95 CU 5/32X800#DR | 662303514778 |
| 229DF08 | 95 CU 1/16X36 F1 MIL | 662303668549 |
| 2291F10 | 95 CU 3/32X36 | 662303510916 |
| 2291F12 | 95 CU 1/8X36 | 662303510923 |
| 2294F30 | 95 CU 3/32X65#CL | 662303510978 |
| 2294F32 | 95 CU 1/8X65#CL | 662303510985 |
| 2294F34 | 95 CU 5/32X65#CL | 662303510992 |
| 2295F32 | 95 CU 1/8X200#CL | 662303523176 |
| 2298F65 | 95 CU 035X35#SP | 662303520410 |
| 2298F66 | 95 CU 040X35#SP | 662303668280 |
| 2298F67 | 95 CU 045X35#SP | 662303511043 |
| 2298F68 | 95 CU 1/16X35#SP | 662303520403 |
| 229DF28 | 95 CU 1/16X36 F2 MIL | 000000000000 |
| 229DF48 | 95 CU 1/16X18X20#CT F1 MIL | 662303521677 |
| 229DF50 | 95 CU 3/32X18 S/C MIL F1 | 662303520311 |
| 229DF68 | 95 CU 1/16X12X10#CT F1 MIL | 662303511104 |
| 229EFBC | 95 CU 035X25#SP MIL | 662303668495 |
| 229EFBD | 95 CU 035X35#SP MIL | 662303511128 |
| 229EFBS | 95 CU 035X11#SP MIL | 662303522483 |
| 229EFDC | 95 CU 045X25#SP MIL | 662303520236 |
| 229EFDD | 95 CU 045X35#SP MIL | 662303511142 |
| 229EFDS | 95 CU 045X11#SP MIL | 662303520151 |
| 229EFDSBI | 95 CU 045X11#SP/44# MIL BATH | 662303523183 |
| 229EFDY | 95 CU 045X60#SP MIL | 662303511159 |
| 229EFEC | 95 CU 1/16X25#SP MIL | 662303668679 |
| 229EFED | 95 CU 1/16X35#SP MIL | 662303511173 |
| 229EFGD | 95 CU 3/32X35#SP MIL | 662303511197 |
| 229EFGE | 95 CU 3/32X65#CL MIL | 662303668624 |
| 229EFHE | 95 CU 1/8X65#CL MIL | 662303668242 |
| 229EFHEBI | 95 CU 1/8X65#CL MIL BATH | 662303668556 |
| 229EFJE | 95 CU 5/32X65#CL MIL | 662303668037 |
| 2312F28 | 95 BARE 1/16X35#SP | 662303511272 |
| 231EFHE | 95 BARE 1/8X65#CL MIL | 662303512644 |
| 231EFHEBI | 95 BARE 1/8X65#CL MIL BATH | 662303523244 |
SAW
Accessories
Depositions/Paramaters
| Diameter | Amps | Deposition Rate | Average Deposition Efficiency |
|---|---|---|---|
| 1/16 in, 1.6 mm | 400 | 13.0 lbs./hr., 5.90 kg./hr. | 99 % |
| 500 | 17.0 lbs./hr., 7.71 kg./hr. | 99 % | |
| 5/64 in, 2.0 mm | 300 | 10.8 lbs./hr., 4.90 kg./hr. | 99 % |
| 400 | 14.5 lbs./hr., 6.58 kg./hr. | 99 % | |
| 500 | 18.2 lbs./hr., 8.26 kg./hr. | 99 % | |
| 3/32 in, 2.4 mm | 400 | 13.2 lbs./hr., 5.99 kg./hr. | 99 % |
| 500 | 17.0 lbs./hr., 7.71 kg./hr. | 99 % | |
| 600 | 22.0 lbs./hr., 9.98 kg./hr. | 99 % | |
| 1/8 in, 3.2 mm | 400 | 11.0 lbs./hr., 4.99 kg./hr. | 99 % |
| 500 | 14.5 lbs./hr., 6.58 kg./hr. | 99 % | |
| 600 | 18.0 lbs./hr., 8.16 kg./hr. | 99 % | |
| 700 | 21.2 lbs./hr., 9.62 kg./hr. | 99 % | |
| 5/32 in, 4.0 mm | 500 | 12.5 lbs./hr., 5.67 kg./hr. | 99 % |
| 600 | 16.0 lbs./hr., 7.26 kg./hr. | 99 % | |
| 700 | 19.5 lbs./hr., 8.85 kg./hr. | 99 % | |
| 800 | 23.0 lbs./hr., 10.43 kg./hr. | 99 % | |
| 900 | 26.0 lbs./hr., 11.79 kg./hr. | 99 % | |
| 3/16 in, 4.8 mm | 600 | 13.9 lbs./hr., 6.31 kg./hr. | 99 % |
| 700 | 17.5 lbs./hr., 7.94 kg./hr. | 99 % | |
| 800 | 21.0 lbs./hr., 9.53 kg./hr. | 99 % | |
| 900 | 25.0 lbs./hr., 11.34 kg./hr. | 99 % | |
| 1000 | 29.2 lbs./hr., 13.25 kg./hr. | 99 % | |
| 1100 | 34.0 lbs./hr., 15.42 kg./hr. | 99 % |
| Diameter | Wire Feed Speed | Amps | Volts | Deposition Rate |
|---|---|---|---|---|
| .023 in, 0.6 mm | 150 ipm, 381 cm/min | 45 | 14 | 1 lbs./hr., 0.4 kg./hr. |
| 200 ipm, 508 cm/min | 55 | 14 | 1.3 lbs./hr., 0.6 kg./hr. | |
| 250 ipm, 635 cm/min | 65 | 15 | 1.6 lbs./hr., 0.7 kg./hr. | |
| 300 ipm, 762 cm/min | 74 | 15 | 2 lbs./hr., 0.9 kg./hr. | |
| 350 ipm, 889 cm/min | 84 | 16 | 2.3 lbs./hr., 1 kg./hr. | |
| 380 ipm, 965 cm/min | 90 | 16 | 2.5 lbs./hr., 1.1 kg./hr. | |
| .030 in, 0.8 mm | 150 ipm, 381 cm/min | 60 | 14 | 1.7 lbs./hr., 0.8 kg./hr. |
| 200 ipm, 508 cm/min | 80 | 15 | 2.2 lbs./hr., 1 kg./hr. | |
| 250 ipm, 635 cm/min | 100 | 15 | 2.8 lbs./hr., 1.3 kg./hr. | |
| 300 ipm, 762 cm/min | 120 | 16 | 3.3 lbs./hr., 1.5 kg./hr. | |
| 350 ipm, 889 cm/min | 140 | 16 | 3.9 lbs./hr., 1.8 kg./hr. | |
| 360 ipm, 914 cm/min | 144 | 16 | 4 lbs./hr., 1.8 kg./hr. | |
| .035 in, 0.9 mm | 180 ipm, 457 cm/min | 90 | 15 | 2.7 lbs./hr., 1.2 kg./hr. |
| 220 ipm, 559 cm/min | 113 | 16 | 3.3 lbs./hr., 1.5 kg./hr. | |
| 260 ipm, 660 cm/min | 137 | 18 | 4 lbs./hr., 1.8 kg./hr. | |
| 300 ipm, 762 cm/min | 160 | 19 | 4.6 lbs./hr., 2.1 kg./hr. | |
| .045 in, 1.2 mm | 125 ipm, 318 cm/min | 130 | 17 | 3.1 lbs./hr., 1.4 kg./hr. |
| 160 ipm, 406 cm/min | 163 | 18 | 4 lbs./hr., 1.8 kg./hr. | |
| 200 ipm, 508 cm/min | 200 | 19 | 5 lbs./hr., 2.3 kg./hr. | |
| .052 in, 1.3 mm | 135 ipm, 343 cm/min | 150 | 17 | 4.5 lbs./hr., 2.1 kg./hr. |
| 190 ipm, 483 cm/min | 200 | 20 | 6.4 lbs./hr., 2.9 kg./hr. | |
| 160 ipm, 406 cm/min | 173 | 18 | 5.4 lbs./hr., 2.4 kg./hr. |
Extra Info
Designed for single or multipass welding where high strength and impact toughness are required. Primary use for military grade steels such as HY-80. This wire meets Military Type 100S-1, MIL-E-23765/2 specifications. Applications include military tanks, ships and other similar fabrication. Used with OK Flux 10.62