PRODUCT SEARCH
SUREWELD 70 LA-2
Sureweld 70 LA-2 conttttttiene una lima revestida especial que permite soldaduras libre de problemas en aceros "difíciles"
Features
Sureweld 70 LA-2 conttttttiene una lima revestida especial que permite soldaduras libre de problemas en aceros "difíciles" como los de alto carbono, alto sulfuro, maquinado libre y aceros rolados en frío. Altos amperajes con el correspondiente alto rango de deposición lo hace más económico que los tipos convencionales en trabajo pesado.
View large imageClassifications
Classifications/Approvals
- ASME SFA 5.1
Properties
| As Welded | |
|---|---|
| Yield Strength | 71 ksi, 495 MPa |
| Tensile Strength | 83 ksi, 575 MPa |
| Reduction in Area | 75 % |
| Elongation in 2" | 28 % |
| Typical Charpy V-Notch Impact Properties | |
| Testing Temperature -20ºF (-29ºC) | |
| As Welded | 35 ft.-lbs., 47 J |
| Typical Undiluted Weld Metal Analysis | |
| C | 0.07 % |
| Mn | 0.9 % |
| Si | 0.5 % |
| P | 0.007 % |
| S | 0.016 % |
SAW
Accessories
Depositions
| Diameter | Optimal Amperage | Range Amperage | Deposition Rate | Efficiency |
|---|---|---|---|---|
| 3/32 in, 2.4 mm | 75 A | 70 - 100 | 1.6 lbs./hr., 0.7 kg./hr. | 73 % |
| 1/8 in, 3.2 mm | 100 A | 110 - 140 | 1.7 lbs./hr., 0.8 kg./hr. | 63.9 % |
| 130 A | 110 - 140 | 2.3 lbs./hr., 1 kg./hr. | 65.8 % | |
| 5/32 in, 4.0 mm | 140 A | 140 - 200 | 3 lbs./hr., 1.4 kg./hr. | 70.5 % |
| 160 A | 140 - 200 | 3.2 lbs./hr., 1.5 kg./hr. | 69.1 % | |
| 190 A | 140 - 200 | 3.6 lbs./hr., 1.6 kg./hr. | 66 % | |
| 3/16 in, 4.8 mm | 175 A | 175 - 250 | 3.8 lbs./hr., 1.7 kg./hr. | 71 % |
| 200 A | 175 - 250 | 4.2 lbs./hr., 1.9 kg./hr. | 71 % | |
| 225 A | 175 - 250 | 4.4 lbs./hr., 2 kg./hr. | 70 % | |
| 250 A | 175 - 250 | 4.8 lbs./hr., 2.2 kg./hr. | 65.8 % | |
| 1/4 in, 6.4 mm | 250 A | 300 - 350 | 5.9 lbs./hr., 2.7 kg./hr. | 74.5 % |
| 275 A | 300 - 350 | 6.4 lbs./hr., 2.9 kg./hr. | 74.1 % | |
| 300 A | 300 - 350 | 6.8 lbs./hr., 3.1 kg./hr. | 73.2 % | |
| 350 A | 300 - 350 | 7.6 lbs./hr., 3.4 kg./hr. | 71.5 % |
Extra Info
Procedure
- For best results, hold a close arc and use as much heat as the nature of the work permits. Avoid wide weaving and maintain a molten pool at all times during welding. Avoid a cold start by striking the arc slightly ahead of the intended start of the weld, wait for the arc to stabilize, and then bring it back to the desired starting point before progressing forward.